TECHNYL 4EARTH C2E 219 MT20 V10 BK H（ECONAMID FL 6GM3010H1 BK）
TECHNYL® 4EARTH C2E 219 MT20 V10 BK H
📌 Product Identification & Sustainability Features
| Polymer Type | Recycled PA6 (Polyamide 6) |
| ISO 1043 Abbreviation | PA6-(GF10+MD20) |
| ISO 16396 Designation | PA6,(GF+MD)30(R100),M1H,S14-060 |
| Processing Technology | Injection Molding |
| Certifications | RoHS |
| Color Available | Black (BK) |
| Formerly Known As | ECONAMID FL 6GM3010H1 BK |
✅ Sustainable Material — 100% Recycled PA6 Base (R100)
✅ 10% Glass Fiber + 20% Mineral — Low Anisotropy, Low Warpage
✅ Heat-Aging Stabilized
✅ Organic Heat Stabilized
✅ High Flowability — MVR 75 cm³/10min
✅ RoHS Compliant
⚡ Physical Properties
🔧 Mechanical Properties
| Property | DAM | Cond.* |
|---|---|---|
| Tensile Modulus (1 mm/min) | 6000 MPa | 3500 MPa |
| Stress at Break (5 mm/min) | 100 MPa | 60 MPa |
| Strain at Break (5 mm/min) | 3% | 10% |
| Flexural Modulus (ISO 178, 2 mm/min) | 5300 MPa | — |
| Flexural Strength (ISO 178, 2 mm/min) | 150 MPa | — |
| Charpy Impact Strength (+23°C) | 30 kJ/m² | 90 kJ/m² |
| Charpy Notched Impact (+23°C) | 5 kJ/m² | 10 kJ/m² |
| Izod Impact Strength (+23°C) | 25 kJ/m² | 85 kJ/m² |
| Izod Notched Impact (+23°C) | 4.5 kJ/m² | 10 kJ/m² |
* Conditioned according to ISO 1110
• Hybrid Reinforcement (MT20): 10% glass fiber provides rigidity, while 20% mineral filler reduces anisotropy, resulting in low warpage and excellent dimensional stability.
• Good Balanced Rigidity: Dry tensile modulus of 6000 MPa and flexural modulus of 5300 MPa meet medium-load structural requirements.
• High Toughness After Conditioning: Strain at break increases from 3% to 10%, notched impact increases from 5 to 10 kJ/m², and Charpy impact jumps from 30 to 90 kJ/m².
• High Flowability: MVR of 75 cm³/10min (275°C/5kg) enables complex thin-wall injection molding.
🌡️ Thermal Properties
| Melting Temperature (10°C/min) | 221°C |
| HDT (0.45 MPa) | 205°C |
| HDT (1.80 MPa) | 175°C |
| Vicat Softening Temperature (50°C/h – 50N) | 200°C |
• Melting point of 221°C, within standard PA6 processing range.
• HDT of 175°C (1.8 MPa) — mineral filler enhances heat deflection temperature.
• Organic heat stabilization system ensures long-term service reliability without heavy metals.
⚡ Electrical Properties
| Volume Resistivity | 1.0 × 10¹³ Ω·m |
| Surface Resistivity | 1.0 × 10¹³ Ω |
🔥 Burning Behaviour
| Flammability (0.75 mm) | HB Rating (UL 94) |
| Burning Rate (FMVSS, Thickness 1 mm) | < 100 mm/min |
🔧 Processing Conditions
• Drying Temperature/Time: 75-85°C / 2-4 hours
• Dew Point Requirement: < -30°C
• Suggested Max Moisture: 0.2%
• Material is supplied in airtight bags, ready for use. If moisture absorption occurs, use dehumidified drying equipment.
Recommended Melt Temperature:
• 240 – 270°C
Recommended Mold Temperature:
• 80 – 90°C
• Up to 120°C for high surface quality requirements
The “MT20” designation stands for 20% mineral reinforcement. Compared to traditional glass fiber-only reinforcement, the glass+mineral hybrid system offers unique advantages:
📐 Reduced Anisotropy: Random orientation of mineral platelets balances the orientation effects of glass fibers, significantly reducing shrinkage differences between parallel and normal directions.
🔄 Excellent Dimensional Stability: Hybrid system minimizes part warpage, ideal for flat, box-shaped components with high flatness requirements.
💰 Cost Efficiency: Mineral fillers are more cost-effective than glass fibers, optimizing material cost while maintaining performance.
✨ Improved Surface Quality: Mineral addition reduces glass fiber exposure, resulting in a smoother part surface.
The “C2E” designation indicates the material contains recycled content. “R100” in the ISO 16396 designation signifies 100% recycled base polymer. This grade was formerly known as ECONAMID FL 6GM3010H1 BK and has been integrated into the TECHNYL 4EARTH product line.
Sustainability Advantages:
• Reduced Carbon Footprint: Significantly lower CO₂ emissions compared to virgin PA6 GF/MD30
• Resource Circularity: Giving new life to post-industrial waste
• No Performance Compromise: Mechanical properties equivalent to virgin materials
• Regulatory Compliance: RoHS compliant
📋 Product Renaming Information
This grade was formerly known as ECONAMID FL 6GM3010H1 BK. Domo has integrated it into the TECHNYL 4EARTH sustainable product line. The new designation C2E 219 MT20 V10 BK H more clearly reflects the product characteristics and technology platform. The material formulation and properties remain unchanged — customers can confidently transition to the new name.
🔧 Typical Applications